Elettra-Sincrotrone Trieste S.C.p.A. website uses session cookies which are required for users to navigate appropriately and safely. Session cookies created by the Elettra-Sincrotrone Trieste S.C.p.A. website navigation do not affect users' privacy during their browsing experience on our website, as they do not entail processing their personal identification data. Session cookies are not permanently stored and indeed are cancelled when the connection to the Elettra-Sincrotrone Trieste S.C.p.A. website is terminated.
More info
OK

Structure of Sm- and Gd-doped ceria


In this study some still unexplained structural features of RE-doped ceria (RE≡Sm or Gd) are clarified by the use
of synchrotron x-ray powder diffraction. Two structural models properly fit experimental data, namely a fluoritic one, resembling the CeO2
 structure at low RE content, and a hybrid one, intermediate between CeO  and cubic RE2O3, at higher rare earth content.

C. Artini et al., Inorg. Chem. 54, 4126 (2015)


A structural study of Sm- and Gd-doped ceria was performed with the aim to clarify some unexplained structural features. (Ce1–xREx)O2–x/2 samples (RE ≡ Sm, Gd; x = 0, 0.1, ..., 1) were prepared by coprecipitation of mixed oxalates and subsequent thermal treatment at 1473, 1173, or 1073 K in air; they were then analyzed at room temperature both by synchrotron X-ray diffraction and μ-Raman spectroscopy. Two structural models were adopted to fit the experimental data, namely, a fluoritic one, resembling the CeO2 structure at low RE content, and a hybrid one at higher RE content, intermediate between the CeO2 and the RE2O3 structures. Two main transitions were detected along the compositional range: (a) an RE-dependent transition at the boundary between the fluoritic and the hybrid regions, of a chemical nature; (b) an RE-independent transition within the hybrid region at ∼0.5, having a purely geometrical nature.
The presence of two finely interlaced F- and C-based structures within the hybrid region was confirmed, and hints of their composition were obtained by μ-Raman spectroscopy. The obtained results indicate a possible explanation for the non-Vegard behavioral trend of the cell parameters.

Retrieve article
Structural features of Sm- and Gd-doped ceria studied by synchrotron X-ray diffraction and -raman spectroscopy;
Cristina Artini, Marcella Pani, Maria M. Carnasciali, Maria T. Buscaglia, Jasper R. Plaisier and Giorgio A. Costa,
Inorganic Chemistry 54, 4126 (2015) 